CH Refractories manufactured magnesite chrome bricks are made from high purity raw material, and divided into magnesite chrome brick, directly bonded magnesite brick and semi-rebonded magnesite chrome brick. All with stable performance and best price.
The refractory magnesia chrome refractory brick is a product made of high-purity magnesia and imported chrome concentrate, which is made by adding a small amount of additives and high pressure and high temperature. Generally there are three different magnesia chrome refractory bricks according to manufacturing method, which are:
1. Common magnesite chrome refractory brick is made by sintered magnesia and refractory level chrome ore as raw materials. The space between refractory grains is bonded with silicate.
2. Direct-bonded magnesite chrome refractory brick is made by chrome ore with low content of impurities and pure magnesite,firing at the temperature above 1700°C.
3. Semi-rebonded and fuse-rebonded magnesite chrome refractory brick are made by fused magnesite chrome sinter.
CH Refractories will suggest you the most suitable and economical magnesia chrome refractory brick according to your kiln or furnace casting condition to save your money and achieve the best performance.
◆Furnace of incineration of garbage
◆Furnaces of chemical industry and construction industry.
◆CFB (circulating fluidized bed) and heat treatment furnace
◆Customerize mould according to different size requirements for free
◆Free sample，Free construction guidance ，free 3D design
◆Low bulk density, low thermal conductivity, good thermal insulation performance.
◆Good integrity with furnace lining, long service life, easy operation, could be shaped freely
◆Wear resistance,cheapest price,high strength at high temperature，high purity raw material
| Items | CH-ZMGe | CH-ZMGe | CH-ZMGe | CH-ZMGe | CH-ZMGe | CH-ZMGe | ||||||
| / | 20A | 20B | 18A | 18B | 16A | 16B | 14A | 14B | 12A | 12B | 8A | 8B |
| Mgo% ≥ | 45 | 40 | 50 | 45 | 52 | 47 | 60 | 55 | 65 | 60 | 65 | 60 |
| Cr2O3% ≥ | 30 | 30 | 26 | 26 | 24 | 24 | 20 | 20 | 16 | 16 | 16 | 16 |
| Fe2O3% | 8-15 | 8-15 | 7-15 | 7-13 | 6-13 | 6-13 | 5-13 | 5-13 | 5-12 | 5-12 | 5-12 | 5-12 |
| SiO2% ≤ | 1.5 | 2.5 | 1.5 | 2.5 | 1.5 | 2.5 | 1.5 | 2.5 | 1.5 | 2.5 | 1.5 | 2.5 |
| Apparent porosity/% ≤ | 15 | 16 | 15 | 16 | 15 | 16 | 15 | 16 | 15 | 16 | 15 | 16 |
| Bulk density g/cm3 ≥ | 3.38 | 3.38 | 3.33 | 3.33 | 3.30 | 3.30 | 3.25 | 3.25 | 3.20 | 3.20 | 3.20 | 3.20 |
| CCS /MPa ≥ | 50 | 50 | 50 | 50 | 50 | 50 | 50 | 50 | 50 | 50 | 50 | 50 |
| 0.2MPa refractoriness under load ≥ | 1700 | 1700 | 1700 | 1700 | 1700 | 1700 | 1700 | 1700 | 1700 | 1700 | 1700 | 1700 |